Carbon Steel C15

C15 is a plain carbon steel with a nominal 0.15% carbon content. It is a relatively low strength steel but it may be quenched and tempered for increased streng

Chemical Composition

Element Min Max
Carbon, C -.– 0.20
Manganese, Mn -.– 0.80
Silicon, Si -.– 0.10
Sulfur, S -.– 0.06
Phosphorous, P -.– 0.06

Mechanical Properties

Nominal thickness (mm) 5 –10 10–16 16 -40 40 -63 63 -100
Rm - Tensile strength (MPa) (+C) 500-800 480-780 430-730 380-670 340-600
Nominal thickness (mm) 5 –10 10–16 16 -40 40 -63 63 -100
Rp0.2 0.2% proof strength (MPa) (+C) 380 340 280 240 215
Nominal thickness (mm) 5 –10 10–16 16 -40 40 -63 63 -100
A - Min. elongation at fracture (%) (+C) 7 8 9 11 12
Brinell hardness (HBW): (+SH) 98 - 178
20-100°C 20-100°C
11 11.8

Physical Properties(avarage values) at ambient temperature

Properties Metric
Modulus of elasticity [10^3x N/mm2] 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m.11] 58.6
Electric resistivity [Ohm mm2/m]: 0.11
Specific heat capacity[lig.11] 0.46
Application

The low carbon steels, such as C15 are used for applications such as cold headed fasteners and bolts.

Stress Annealing

Stress relieving to remove machining stresses should be carried out by heating to approx. 540°C, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment

Machinability

Machinability of C15 steel is fairly good, especially in the cold drawn or cold worked condition. Based upon carbon steel AIS11112 as a reference that is considered 100% machinable (easily machined) the C10 steel has a rating of 55%.

+A Soft annealed
+AC Annealed to achieve spheroidization of the carbides
_+AR As rolled
+AT Solution annealed
+C Cold drawn / hard
+CR Cold rolled
+FP Treated to ferrite-pearlite structure and hardness range
+I Isothermal annealing
+LC Cold drawn / soft
+M Thermo mechanical rolling
+N Normalized
+NT Normalized and tempered
+P Precipitation hardened
+PE Peeled
+QA Air quenched and tempered
+QL Liquid quenched and tempered
+QT Quenched and tempered
+S Treated to improve shearability
+SH As rolled and turned
+SR Cold drawn and stress relieved
+T Tempered
+TH Treated to hardness range
+WW Warm worked
+U Untreated